首页 > Products > stainless steel plate > 310/310S Stainless steel plate
Product Introduction：
310 stainless steel austenitic chromium nickel stainless steel has good oxidation resistance, corrosion resistance, because the higher percentage of chromium and nickel, 310 has much better creep strength, can continuously work under high temperature, good heat resistance.310S stainless steel is austenitic chromium-nickel stainless steel, has a good 310S stainless steel oxidation resistance, resistance Corrosive.
Because of the high percentage of chromium and nickel, which has a much better creep strength, can continue to work at high temperatures, with good heat resistance.
Due to the high content of nickel (Ni), and chromium (Cr), good oxidation resistance, corrosion resistance, acid and alkali resistance, high-temperature resistance, high-temperature resistant steel pipe is used in the manufacture of electric furnace tubes and other occasions.
The only difference for 310 310S stainless steel is the 310 stainless steel does not contain sulfur elements. What’s more, the carbon content of 310S is much lower than 310.
Chemical Composition
Grade （材质） | C(%) （碳） | Si(%) （硅） | Mn(%) （锰） | P(%) （磷） | S(%） （硫） | Cr（%） （铬） | Ni(%) （镍） | N(%) （氮） | Cu(%) （铜） |
310 | ≤0.25 | ≤1.0 | ≤2.0 | ≤0.03 | --- | 24.0-26.0 | 19.0-22.0 | --- | --- |
310S | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.03 | ≤0.03 | 24.0-26.0 | 19.0-22.0 | --- | --- |
Mechanical Property
Grade （材质） | tensile strength Mpa （抗拉强度） | Yield Strength Mpa （屈服强度） | Elongation (%) （伸长率） | rate of reduction in area (%) （断面收缩率） | Density (g/cm3) （密度） |
310 | ≥470 | ≥170 | ≥40 | ≥50 | 7.98 |
310S | ≥520 | ≥205 | ≥40 | ≥50 | 7.98 |
Specifications
Technical （工艺） | Thickness （厚度） | Width （宽度） | Finish （表面） | Origin （产地） |
Cold rolled | 0.4mm-3.0mm | Standard:1000mm 1219mm 1500mm Special: can be ordered | 2B / No.4 / HL / BA / Mirror / Checkered / Colored etc | TISCO / ZPSS etc |
Hot rolled | 3.0mm-80.0mm | Standard: 1500mm 1800mm 2000mm Special: can be ordered | No.1 / No.4 / HL / Mirror etc | TISCO/ZPSS etc |
Applications
310 310S stainless steel is the most common choice of boiler materials. Also widely used in stamping dies, fixtures, tools, gauges, paper cutting knives, tools, petroleum, electronics, chemical, pharmaceutical, textile, food, machinery, construction, nuclear power, aerospace, military, and other industries!
Different Production Standards
Grade （材质） | GB/T 1220-2007 （国标） | ASTM （美标） | DIN （欧标） | JIS （日标） | KS （韩国） |
310 | 20Cr25Ni20 | 310 | 1.4821 | SUS310 | STS310 |
310S | 06Cr25Ni20 | 310S | 1.4845 | SUS310S | STS310S |
More about 310/310S
High-temperature oxidation resistance for 310/310S material
310 310S stainless steel through the oxidation of chromium to the local oxidation resistance, in the local oxidation of chromium in process, can form a very stable oxide (Cr2O3 chromium oxide). As long as the chromium content of the metal is, the metal surface can form a continuous layer of chromium oxide green, to prevent the formation of other oxides, and to protect the metal. The oxidation resistance of austenitic stainless steel can be calculated by chromium content. The high-temperature resistant alloy chromium content of at least 20% (weight percent). The use of nickel as a substitute for iron can also provide the properties of alloys at elevated temperatures. 310/310S is a high alloy material, so it has good oxidation resistance.
Heat treatment/annealing for 310/310S material
The main reason for the annealing of these alloys is the formation of a recrystallized fine structure, uniform grain size, and decomposition of harmful chromium carbide precipitates.